TAD Red D124 red

Basic characteristics: 1. Good water solubility 2. Uniform dyeing 3. Stable performance 4. Long service life 5. Excellent weather resistance of dyed aluminum material; 1. When slotting, the dye should be completely dissolved. It is recommended to dissolve it in 80 ℃ water (dye: water=1:5) first. After dissolution, pour it into the dyeing tank and stir evenly before use. If there is dirt during use, it needs to be heated and filtered before use.

Service hotline: +86-18680155273 / +86-18680155273

Details

Number	Information	Light colour	In color	Deep colour
1	TAD D4G YELLOW	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
2	TAD D203 YELLOW	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
3	TAD D201 YELLOW	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
4	TAD D300 ORANGE	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
5	TAD D301 ORANGE	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
6	TAD D302 ORANGE	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
7	TAD D101 RED	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
8	TAD D105 RED	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
9	TAD D106 RED	Concentration: 1 gram/liter Time: 60 seconds Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
10	TAD D102 RED	Concentration: 1.5 g/L Time: 90 seconds 　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
11	TAD D124 RED	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
12	TAD D139 PINK	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
13	TAD D131 PINK	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
14	TAD D144 PINK	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
15	TAD D909 VIOLET	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
16	TAD D910 VIOLET	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
17	TAD D1 GREEN	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
18	TAD D2 GREEN	Concentration: 1.5 g/L Time: 90 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 300 seconds Film thickness: 8 μ M	Concentration: 5 g/L Time: 500 seconds Film thickness: 12 μ M
19	TAD D502 BLUE	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
20	TAD D503 BLUE	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
21	TAD D507 BLUE	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
22	TAD D501 BLUE	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
23	TAD D8 BRONE	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
24	TAD D601 BROWN	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
25	TAD D602 BROWN	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
26	TAD D402 BLACK	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
27	TAD D420 BLACK	Concentration: 2 g/L Time: 120 seconds　Film thickness: 5 μ M	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time: 600 seconds　Film thickness: 12 μ M
28	TAD D414 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
29	TAD D415 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
30	TAD D415AN BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
31	TAD D413 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
32	TAD D421 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
33	TAD D411 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
34	TAD D419 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm
35	TAD D422 BLACK	Concentration: 2 g/L Time:180second　 Film thickness:5μm	Concentration: 3 g/L Time: 360 seconds　Film thickness: 8 μ M	Concentration: 5 g/L Time:900second　 Film thickness:12μm

Basic features:

1. Good water solubility 2. Uniform dyeing 3. Stable performance 4. Long service life 5. Excellent weather resistance of aluminum material after dyeing

Kind reminder:

1. When slotting, the dye should be completely dissolved. It is recommended to dissolve it in 80 ℃ water (dye: water=1:5) first. After dissolution, pour it into the dyeing tank and stir evenly before use. If there is dirt during use, it needs to be heated and filtered before use.

2. When opening the cylinder, it is recommended to use a pH stabilizer to buffer the pH value and use it within the standard range;

3. It is recommended to use TAD-500 high-temperature sealing agent for sealing

4. When color matching is required, it is not advisable to match it with other brands of dyes

Packaging: 1KG/bag

TAD Color Guide


	Sample Display
	Aluminium Alloy	（A1050P)
Process	Product Model		Concentration	Temperature	Time
Degreasing	TAD 208C Aluminium Alloy Degreasing Powder		50g/L	50-80℃	5 Minutes
Alkaline Etching	TAD 140 Alkaline Etching Additive		3g/L	50℃	30second　 30 Seconds
	NaOH		70g/L
Chemical Polishing	89% Phosphoric Acid		700ml/L	105℃	20second
	98% Sulphric Acid		300ml/L
Ash Removing	TAD 830 Enviromental Ash Removing Additive		80ml/L	Normal Temperature	30 Seconds
Anodizing Oxidation	98% Sulphric Acid		200g/L	21℃	20-50 Minutes
	Oxidation Film Thickness		Light Color 5μm	Middle Color 8μm	Deep Color 12μm
Activation	TAD 999 Dye Pre-treatment Additive		50g/L	Normal Temperature	5 Minutes
Color Dye	Pls. refer to TAD COLOR USING INSTRUCTION.
Sealing	TAD 500 High Temperature Sealing Additive		10g/L	90℃	15 Minutes
Above is just the processing conditions for colors display, the specific situation should be decided by user tests to confirm.